SINOSTEEL MAANSHAN NEW MATERIAL TECHNOLOGY CO.,LTD is a National Torch Program High-tech Enterprise. It has outstandingly completed a series of major national scientific and technological tasks from "the Sixth Five-year" to "the Eleventh Five-Year", and published over 2,500 academic papers at home and abroad. It owns all kinds of equipment and facilities consisting of more than 1,700 (sets), and over 50 supporting pilot plants...

Home  >> Products  >> Application of Hollow glass beads in paint(coating)

Application of Hollow glass beads in paint(coating)

Send Inquiry

Download

  • Technical parameters
  • Applications
  • Storage and Handling
  • Health and Safety Information

Detailed Product Description


1.Improve flow properties
2.A superior substitute of resin
3.Low shrinkage and warpage
4.More economical
5.Adjusting density

Application of Hollow glass microspheres in paint.

 

Appearance:      White fine powder

Particle shape:  Hollow sphere

Composition:     Soda lime borosilicate quality

True density:    0.25-0.60g/cc

Average particle size: about2-120 μm

Compressive strength:  about 4-69MPa

Thermal conductivity:  0.03-0.06w/m.k

 

1.Glass microspheres have the smallest surface area and low oil absorption rate, can significantly reduce the consumption of other components in paint.

2.The vitrified surface of glass microspheres can realize the chemical corrosion resistant, and reflexaction on light. Therefore, the painting coating can prevent from fouling, corrosion, UV,

yellowing and scratching etc.

3.Thin gas inside the hollow glass microspheres with compact arrangement, makes low thermal conductivity, so that paint coating has a very good effect on heat insulation.

4.Hollow glass microspheres can effectively enhance the fluidity and smoothness of coating.

5.Hollow glass microspheres contain gas inside, so it has a good contractility resistance to hot and cold, thus enhancing the flexibility of coating, greatly reducing the cracking and peeling

of the coating due to thermal expansion and contraction.

6.On premise of high filling level, the viscosity of paint will not be significantly increased, thus reducing the usage of solvents. It can reduce toxic gas emissions in the process of

painting, and VOC indicator can be effectively reduced.

Dosage recommendation:

The addition is normally about 10-20% of the total weight.

Adding methods are proposed as follows:  Last step.

The hollow glass microspheres are proposed to add at the last step, and dispersed with low-speed, low shearing force mixing equipment. Due to its good liquidity, the spherical balls have less

friction between each other, and are easily dispersed into mixture to completely keep wet within a short time. Through slightly extending mixing time can achieve uniform dispersion.
Hollow glass microspheres are inert and non-toxic. Due to its light weight, attention should be specially paid when adding. We recommend adding the beads by step, that is, the addition

quantity is 1 / 2 of the remaining beads each time. It can well avoid the beads floating into the air and make it disperse even more completely.

Type 

Color

 

Particles diameter

μm

 

True density

g/cm3

 

 Pressure resistance

MPa

T15

 white

2-120

0.15

1.5

T20

white

2-110

0.20

3

T25

white

2-110

0.25

5

T32

white

2-90

0.32

12

T40

white

2-85

0.40

28

T46

white

2-80

0.46

34

T60

white

2-65

0.60

58